NDH Jacket of telephone cable,RF cable and optical cable
LDH Jacket of telephone cable and optical cable
MH Jacket of optical cable ,aerial cable and power cable
GH Jacket of optical cable. High strength and abrasion resistant jacket
NLDJ Insulation of aerial cable ,less than 1kV
NGJ Insulation of aerial cable
ZPE Flame retardant insulating or jacket of 70~90 ℃ wires and cables
RDH Flexible PE jacket of 70 ℃ wires and cables
sabic plastic raw materials
| No. | Property | Unit | Test | JY102 |
| 1 | Melt Flow Index | g/10min | GB/T3682-2000 | ≤2.0 |
| 2 | Density | g/cm3 | GB/T1033.1-2008 | ≤0.945 |
| 3 | Tensile strength | Mpa | GB/T1040.3-2006 | ≥13.0 |
| 4 | Tensile yield strength | Mpa | GB/T1040.3-2006 | -- |
| 5 | Elongation at break | % | GB/T1040.3-2006 | ≥500 |
| 6 | Brittle temperature at low temperature | ℃ | GB/T5470-2008 | ≤-76 |
| 7 | ESCR ,FO | H | GB/T2951.41-2008 | ≥96 |
| 8 | Oxidation induction period at 200℃ | Min | GB/T2951.42-2008 | ≥30 |
| 9 | Content of Carbon black | % | GB/T2951.41-2008 | 2.60±0.25 |
| 10 | Carbon Black dispersion | -- | GB/T18251-2000 | ≤3 |
| 11 | Ceka softening point | ℃ | GB/T1633-2000 | -- |
| 12 | Tensile strength after thermal aging | Mpa | GB/T2951.12-2008 | -- |
| 12 | Elongation after thermal aging | % | GB/T2951.12-2008 | -- |
| 13 | Elongation at Low Temperature | % | GB/T2951.14-2008 | -- |
| 16 | Dielectric strength | Mv/m | GB/T1408.1-2006 | ≥25 |
| 17 | Volume resistivity | Ω.m | GB/T1410-2006 | ≥1*1014 |
| 18 | Dielectric Constant | -- | GB/T1409-2006 | ≤2.80 |